What consequence results when solidification shrinkage in investment casting restricts the gating system?

💡 Explanation

Increased porosity arises because volumetric contraction during solidification leads to voids, due to obstructed feeding of molten metal affected by the _directional solidification_ mechanism; therefore porosity increases rather than decreases, because gating blockage inhibits complete filling of the cavity.