Which limit increased brittle failures in early cast iron?

💡 Explanation

In early cast iron, high phosphorus segregated at grain boundaries, promoting brittle fracture through grain boundary embrittlement by forming iron phosphide precipitates because stress concentrates along these weakened interfaces therefore leading to intergranular cracking rather than ductile deformation.