Which outcome results when internal stresses exceed bond energies in amorphous silica?

💡 Explanation

Fracturing results because bond breakage via stress corrosion cracking exceeds bond energies, releasing stored elastic strain, therefore macroscopic cracks form rather than ductile deformation because amorphous silica cannot relieve stress via dislocation slip.