Which outcome occurs when mismatched crystalline semiconductor layers grow?

💡 Explanation

The unequal lattice constants result in strain; therefore, threading dislocations form, due to strain relief via introduction of line defects in the crystal rather than uniform compression because that would require higher energy input.