Which shrinkage risk escalates when casting large aluminum engine blocks?

💡 Explanation

Hot tearing increases due to inhibited thermal contraction via the columnar solidification caused by the constrained cooling. This is a form of thermal stress relief around internal risers. Therefore, localized cracking occurs earlier rather than uniform shrinkage.